Forming Quality and Fatigue Behavior of Self-Piercing Riveted Joints of DP590 and AA6061 Plates
Two kinds of self-piercing riveted (SPR) joints were prepared with DP590 and AA6061 plates. The forming qualities of the joints were studied using the finite element method. The relationships between the fatigue life and failure forms of the joints with different upper plates were discussed. Finally...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2021-01-01
|
| Series: | Advances in Materials Science and Engineering |
| Online Access: | http://dx.doi.org/10.1155/2021/4381544 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1841524688755359744 |
|---|---|
| author | Yinglian Jia Zhichao Huang Yongchao Zhang Fan Zhang |
| author_facet | Yinglian Jia Zhichao Huang Yongchao Zhang Fan Zhang |
| author_sort | Yinglian Jia |
| collection | DOAJ |
| description | Two kinds of self-piercing riveted (SPR) joints were prepared with DP590 and AA6061 plates. The forming qualities of the joints were studied using the finite element method. The relationships between the fatigue life and failure forms of the joints with different upper plates were discussed. Finally, the failure mechanisms of the joints were analyzed. The results show that the maximum static tension of DA32 joints (with an upper plate of DP590) is significantly greater than that of the other kind, and the fatigue life of DA32 joints is always longer than that of AA40 joints when with a 2.0 mm thick AA6061 aluminum alloy upper plate under the same fatigue load. The failure mode of SPR joints changes obviously due to different upper plates, and the fatigue life of the joints can be effectively improved by reducing the microvibration wear. |
| format | Article |
| id | doaj-art-8d88f8e05707492896391c2410677eeb |
| institution | Kabale University |
| issn | 1687-8434 1687-8442 |
| language | English |
| publishDate | 2021-01-01 |
| publisher | Wiley |
| record_format | Article |
| series | Advances in Materials Science and Engineering |
| spelling | doaj-art-8d88f8e05707492896391c2410677eeb2025-02-03T05:47:37ZengWileyAdvances in Materials Science and Engineering1687-84341687-84422021-01-01202110.1155/2021/43815444381544Forming Quality and Fatigue Behavior of Self-Piercing Riveted Joints of DP590 and AA6061 PlatesYinglian Jia0Zhichao Huang1Yongchao Zhang2Fan Zhang3Key Laboratory for Conveyance and Equipment, Ministry of Education, East China Jiaotong University, Nanchang 330013, ChinaKey Laboratory for Conveyance and Equipment, Ministry of Education, East China Jiaotong University, Nanchang 330013, ChinaKey Laboratory for Conveyance and Equipment, Ministry of Education, East China Jiaotong University, Nanchang 330013, ChinaKey Laboratory for Conveyance and Equipment, Ministry of Education, East China Jiaotong University, Nanchang 330013, ChinaTwo kinds of self-piercing riveted (SPR) joints were prepared with DP590 and AA6061 plates. The forming qualities of the joints were studied using the finite element method. The relationships between the fatigue life and failure forms of the joints with different upper plates were discussed. Finally, the failure mechanisms of the joints were analyzed. The results show that the maximum static tension of DA32 joints (with an upper plate of DP590) is significantly greater than that of the other kind, and the fatigue life of DA32 joints is always longer than that of AA40 joints when with a 2.0 mm thick AA6061 aluminum alloy upper plate under the same fatigue load. The failure mode of SPR joints changes obviously due to different upper plates, and the fatigue life of the joints can be effectively improved by reducing the microvibration wear.http://dx.doi.org/10.1155/2021/4381544 |
| spellingShingle | Yinglian Jia Zhichao Huang Yongchao Zhang Fan Zhang Forming Quality and Fatigue Behavior of Self-Piercing Riveted Joints of DP590 and AA6061 Plates Advances in Materials Science and Engineering |
| title | Forming Quality and Fatigue Behavior of Self-Piercing Riveted Joints of DP590 and AA6061 Plates |
| title_full | Forming Quality and Fatigue Behavior of Self-Piercing Riveted Joints of DP590 and AA6061 Plates |
| title_fullStr | Forming Quality and Fatigue Behavior of Self-Piercing Riveted Joints of DP590 and AA6061 Plates |
| title_full_unstemmed | Forming Quality and Fatigue Behavior of Self-Piercing Riveted Joints of DP590 and AA6061 Plates |
| title_short | Forming Quality and Fatigue Behavior of Self-Piercing Riveted Joints of DP590 and AA6061 Plates |
| title_sort | forming quality and fatigue behavior of self piercing riveted joints of dp590 and aa6061 plates |
| url | http://dx.doi.org/10.1155/2021/4381544 |
| work_keys_str_mv | AT yinglianjia formingqualityandfatiguebehaviorofselfpiercingrivetedjointsofdp590andaa6061plates AT zhichaohuang formingqualityandfatiguebehaviorofselfpiercingrivetedjointsofdp590andaa6061plates AT yongchaozhang formingqualityandfatiguebehaviorofselfpiercingrivetedjointsofdp590andaa6061plates AT fanzhang formingqualityandfatiguebehaviorofselfpiercingrivetedjointsofdp590andaa6061plates |