RESERACH ON FATIGUE BEHAVIOUR COMPARISON OF ALUMINUM RIVETED JOINT AND FRICTION STIR WELDING JOINT
S-N curves of 2524-T3 parental material,FSW joint,riveted joint were obtained by fatigue test of FSW comparative specimens. Result revealed that firstly fatigue cracks in FSW joints were mostly initiated from bottom of the weld seam. Secondly,fatigue behavior of thin plate was slightly better than t...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Editorial Office of Journal of Mechanical Strength
2015-01-01
|
| Series: | Jixie qiangdu |
| Subjects: | |
| Online Access: | http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2015.03.014 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1841534608405954560 |
|---|---|
| author | ZHANG YanJun LI XiaoPeng |
| author_facet | ZHANG YanJun LI XiaoPeng |
| author_sort | ZHANG YanJun |
| collection | DOAJ |
| description | S-N curves of 2524-T3 parental material,FSW joint,riveted joint were obtained by fatigue test of FSW comparative specimens. Result revealed that firstly fatigue cracks in FSW joints were mostly initiated from bottom of the weld seam. Secondly,fatigue behavior of thin plate was slightly better than that of thick plate. Finally,fatigue behavior of FSW joint was significantly better than that of riveted joint. S-N curves for variable thicknesses and stress ratios were fitted,which provided correlative data for application of FSW technology to aircraft structures. |
| format | Article |
| id | doaj-art-796cb4bc77264525bd28578672f988b7 |
| institution | Kabale University |
| issn | 1001-9669 |
| language | zho |
| publishDate | 2015-01-01 |
| publisher | Editorial Office of Journal of Mechanical Strength |
| record_format | Article |
| series | Jixie qiangdu |
| spelling | doaj-art-796cb4bc77264525bd28578672f988b72025-01-15T02:38:24ZzhoEditorial Office of Journal of Mechanical StrengthJixie qiangdu1001-96692015-01-013742943430591605RESERACH ON FATIGUE BEHAVIOUR COMPARISON OF ALUMINUM RIVETED JOINT AND FRICTION STIR WELDING JOINTZHANG YanJunLI XiaoPengS-N curves of 2524-T3 parental material,FSW joint,riveted joint were obtained by fatigue test of FSW comparative specimens. Result revealed that firstly fatigue cracks in FSW joints were mostly initiated from bottom of the weld seam. Secondly,fatigue behavior of thin plate was slightly better than that of thick plate. Finally,fatigue behavior of FSW joint was significantly better than that of riveted joint. S-N curves for variable thicknesses and stress ratios were fitted,which provided correlative data for application of FSW technology to aircraft structures.http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2015.03.014Aluminum alloyFriction stir weldingJointS-N CurveFatigue |
| spellingShingle | ZHANG YanJun LI XiaoPeng RESERACH ON FATIGUE BEHAVIOUR COMPARISON OF ALUMINUM RIVETED JOINT AND FRICTION STIR WELDING JOINT Jixie qiangdu Aluminum alloy Friction stir welding Joint S-N Curve Fatigue |
| title | RESERACH ON FATIGUE BEHAVIOUR COMPARISON OF ALUMINUM RIVETED JOINT AND FRICTION STIR WELDING JOINT |
| title_full | RESERACH ON FATIGUE BEHAVIOUR COMPARISON OF ALUMINUM RIVETED JOINT AND FRICTION STIR WELDING JOINT |
| title_fullStr | RESERACH ON FATIGUE BEHAVIOUR COMPARISON OF ALUMINUM RIVETED JOINT AND FRICTION STIR WELDING JOINT |
| title_full_unstemmed | RESERACH ON FATIGUE BEHAVIOUR COMPARISON OF ALUMINUM RIVETED JOINT AND FRICTION STIR WELDING JOINT |
| title_short | RESERACH ON FATIGUE BEHAVIOUR COMPARISON OF ALUMINUM RIVETED JOINT AND FRICTION STIR WELDING JOINT |
| title_sort | reserach on fatigue behaviour comparison of aluminum riveted joint and friction stir welding joint |
| topic | Aluminum alloy Friction stir welding Joint S-N Curve Fatigue |
| url | http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2015.03.014 |
| work_keys_str_mv | AT zhangyanjun reserachonfatiguebehaviourcomparisonofaluminumrivetedjointandfrictionstirweldingjoint AT lixiaopeng reserachonfatiguebehaviourcomparisonofaluminumrivetedjointandfrictionstirweldingjoint |