Multiaxial elastoplastic cyclic loading of austenitic 316L steel
Cyclic stress-strain response and fatigue damage character has been investigated in austenitic stainless steel 316L. Hollow cylindrical specimens have been cyclically deformed in combined tension-compression and torsion under constant strain rate condition and different constant strain and shear str...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Gruppo Italiano Frattura
2017-04-01
|
| Series: | Fracture and Structural Integrity |
| Subjects: | |
| Online Access: | https://www.fracturae.com/index.php/fis/article/view/1853 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Cyclic stress-strain response and fatigue damage character has been investigated in austenitic stainless steel 316L. Hollow cylindrical specimens have been cyclically deformed in combined tension-compression and torsion under constant strain rate condition and different constant strain and shear strain amplitudes. In-phase and 90° out-of-phase cyclic straining was applied and the stress response has been monitored. Cyclic hardening/softening curves were assessed in both channels. Cyclic softening followed for higher strain amplitudes by long-term cyclic hardening was observed. Cyclic stress-strain curves were determined. Study of the surface damage in fractured specimens revealed the types and directions of principal cracks and the sources of fatigue crack initiation in slip bands. |
|---|---|
| ISSN: | 1971-8993 |