Cruciform specimens used for determination of the influence of T-stress on fatigue crack growth with overloads on aluminum alloy Al 6061 T651
The publication presents a cruciform specimen for the determination of cyclic crack growth data under biaxial loading. The design of the specimen with slotted loading arms allows good decoupling between the two loading directions. For different initial crack geometries, the solutions for the stress...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Gruppo Italiano Frattura
2019-04-01
|
| Series: | Fracture and Structural Integrity |
| Subjects: | |
| Online Access: | https://www.fracturae.com/index.php/fis/article/view/2313/2504 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1841564215995793408 |
|---|---|
| author | Sebastian Henkel Carl H. Wolf Horst Biermann Andreas Burgold Meinhard Kuna |
| author_facet | Sebastian Henkel Carl H. Wolf Horst Biermann Andreas Burgold Meinhard Kuna |
| author_sort | Sebastian Henkel |
| collection | DOAJ |
| description | The publication presents a cruciform specimen for the determination of cyclic crack growth data under biaxial loading. The design of the specimen with slotted loading arms allows good decoupling between the two loading directions. For different initial crack geometries, the solutions for the stress intensity factors KI and KII as well as the crack-parallel T-stress are calculated by linear elastic finite element analysis (FEA) with the program ABAQUS. For two specimens with the same geometry made of aluminium alloy 6061 T651, the crack growth behaviour is measured at different T-stresses at a stress ratio of R=0.7 and overloads. It is shown that the crack retardation after an overload with crack-parallel tensile stress is less than without it. The reason for this behaviour is considered to be the reduced plasticity at the crack tip due to the higher triaxiality of the stress state. |
| format | Article |
| id | doaj-art-fe2b7d975d624f8c98be9085b4416d89 |
| institution | Kabale University |
| issn | 1971-8993 |
| language | English |
| publishDate | 2019-04-01 |
| publisher | Gruppo Italiano Frattura |
| record_format | Article |
| series | Fracture and Structural Integrity |
| spelling | doaj-art-fe2b7d975d624f8c98be9085b4416d892025-01-02T23:01:34ZengGruppo Italiano FratturaFracture and Structural Integrity1971-89932019-04-01134813514310.3221/IGF-ESIS.48.1610.3221/IGF-ESIS.48.16Cruciform specimens used for determination of the influence of T-stress on fatigue crack growth with overloads on aluminum alloy Al 6061 T651Sebastian HenkelCarl H. WolfHorst BiermannAndreas BurgoldMeinhard KunaThe publication presents a cruciform specimen for the determination of cyclic crack growth data under biaxial loading. The design of the specimen with slotted loading arms allows good decoupling between the two loading directions. For different initial crack geometries, the solutions for the stress intensity factors KI and KII as well as the crack-parallel T-stress are calculated by linear elastic finite element analysis (FEA) with the program ABAQUS. For two specimens with the same geometry made of aluminium alloy 6061 T651, the crack growth behaviour is measured at different T-stresses at a stress ratio of R=0.7 and overloads. It is shown that the crack retardation after an overload with crack-parallel tensile stress is less than without it. The reason for this behaviour is considered to be the reduced plasticity at the crack tip due to the higher triaxiality of the stress state.https://www.fracturae.com/index.php/fis/article/view/2313/2504Cruciform specimenBiaxial testingFracture mechanicsT-stressOverloadFatigue crack growth |
| spellingShingle | Sebastian Henkel Carl H. Wolf Horst Biermann Andreas Burgold Meinhard Kuna Cruciform specimens used for determination of the influence of T-stress on fatigue crack growth with overloads on aluminum alloy Al 6061 T651 Fracture and Structural Integrity Cruciform specimen Biaxial testing Fracture mechanics T-stress Overload Fatigue crack growth |
| title | Cruciform specimens used for determination of the influence of T-stress on fatigue crack growth with overloads on aluminum alloy Al 6061 T651 |
| title_full | Cruciform specimens used for determination of the influence of T-stress on fatigue crack growth with overloads on aluminum alloy Al 6061 T651 |
| title_fullStr | Cruciform specimens used for determination of the influence of T-stress on fatigue crack growth with overloads on aluminum alloy Al 6061 T651 |
| title_full_unstemmed | Cruciform specimens used for determination of the influence of T-stress on fatigue crack growth with overloads on aluminum alloy Al 6061 T651 |
| title_short | Cruciform specimens used for determination of the influence of T-stress on fatigue crack growth with overloads on aluminum alloy Al 6061 T651 |
| title_sort | cruciform specimens used for determination of the influence of t stress on fatigue crack growth with overloads on aluminum alloy al 6061 t651 |
| topic | Cruciform specimen Biaxial testing Fracture mechanics T-stress Overload Fatigue crack growth |
| url | https://www.fracturae.com/index.php/fis/article/view/2313/2504 |
| work_keys_str_mv | AT sebastianhenkel cruciformspecimensusedfordeterminationoftheinfluenceoftstressonfatiguecrackgrowthwithoverloadsonaluminumalloyal6061t651 AT carlhwolf cruciformspecimensusedfordeterminationoftheinfluenceoftstressonfatiguecrackgrowthwithoverloadsonaluminumalloyal6061t651 AT horstbiermann cruciformspecimensusedfordeterminationoftheinfluenceoftstressonfatiguecrackgrowthwithoverloadsonaluminumalloyal6061t651 AT andreasburgold cruciformspecimensusedfordeterminationoftheinfluenceoftstressonfatiguecrackgrowthwithoverloadsonaluminumalloyal6061t651 AT meinhardkuna cruciformspecimensusedfordeterminationoftheinfluenceoftstressonfatiguecrackgrowthwithoverloadsonaluminumalloyal6061t651 |