Failure Analysis of Corrosion-Induced Perforation in B10 Copper-Nickel Alloy Pipelines

Failure Analysis of Corrosion-Induced Perforation in B10 Copper-Nickel Alloy Pipelines

The B10 copper-nickel alloy pipeline used for seawater transportation on a certain platform was found to have corrosion perforation at the weld joint between the elbow and the flange during a shutdown inspection.In this study， the failure mechanism of corrosion perforation was analyzed using macrosc...

Full description

Saved in:

Bibliographic Details
Main Author:	SONG Shuai, QIN Limin, SUN Yujiang, ZHANG Shangfeng, YANG Wenming, HE Yueyang, XU Zhigang
Format:	Article
Language:	zho
Published:	Editorial Department of Materials Protection 2024-12-01
Series:	Cailiao Baohu
Subjects:	b10 copper-nickel alloy； failure analysis； erosion corrosion； intergranular corrosion； dealloying corrosion； seawater
Online Access:	http://www.mat-pro.com/fileup/1001-1560/PDF/20241216.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

Similar Items

Corrosion of Buried Pipelines by Stray Current in Electrified Railways: Mechanism, Influencing Factors, and Protection
by: Haiming Liang, et al.
Published: (2024-12-01)

The influence of gelatine on the corrosion behaviour of cold worked copper wire in alkaline media
by: Ivanov Svetlana, et al.
Published: (2006-01-01)

Study on the Weight and Patterns of Key Controlling Factors for Corrosion in Gathering and Transportation Pipelines of the Sulige Gas Field
by: JIANG Chengyin, LI Qiongwei, BAI Zilong, HAN Zizi, HUI Baoping, ZHANG Ruoyin, LIU Wei
Published: (2024-12-01)

Corrosive behavior of copper canisters under air and aerobic groundwater at early stages of deep geological disposal
by: Junhyuk Jang, et al.
Published: (2025-01-01)

Modelación con elementos finitos del agrietamiento en el hormigón por corrosión localizada en la armadura Finite element modeling of cracking in concrete due to localized corrosion in the reinforcement
by: J Castorena, et al.
Published: (2007-04-01)

Corrosion of steel in ionic liquids
by: Arenas M.F., et al.
Published: (2003-01-01)

Performance of seawater-derived Mg(OH)2 as a sustainable coating solution for hydrogen sulfide-induced corrosion mitigation in concrete pipes
by: Janelle Patricia S. Moa, et al.
Published: (2025-02-01)

SCC and Corrosion Fatigue characterization of a Ti-6Al-4V alloy in a corrosive environment – experiments and numerical models
by: S. Baragetti, et al.
Published: (2014-09-01)

FAILURE ANALYSIS OF HIGH STRENGTH ALUMINUM ALLOY WHEEL
by: YU JianMin, et al.
Published: (2018-01-01)

Insights into the localized corrosion initiation mechanisms of alloy 718
by: Julia Botinha, et al.
Published: (2025-01-01)

Eliminating fluoride-induced corrosion of aluminum cathodes in zinc electrowinning by aluminum ion complexation
by: N.G.S. Almeida, et al.
Published: (2025-01-01)

High-Temporal-Resolution Corrosion Monitoring in Fluctuating-Temperature Environments with an Improved Electrical Resistance Sensor
by: Mao Takeyama
Published: (2025-01-01)

Effect of Trace Rare Earth Elements (Ce) on the Corrosion Resistance of High-Strength Weathering Bridge Steels
by: Jiquan Chen, et al.
Published: (2025-01-01)

A review on bio-inspired corrosion resistant superhydrophobic coating on copper substrate: recent advances, mechanisms, constraints, and future prospects
by: Himanshu Prasad Mamgain, et al.
Published: (2025-03-01)

CRACK PROPAGATION BEHAVIOR OF OIL WELL TUBING STEEL UNDER CORROSION FATIGUE LOADING IN CO<sub>2</sub>-CL-CORROSIVE ENVIRONMENT
by: LI Zhen, et al.
Published: (2016-01-01)

SURFACE HARDENING HEAT TREATMENTS APPLIED TO CAST IRONS AND STEELS USED IN THE MANUFACTURE OF HEAT EXCHANGER SUBASSEMBLIES
by: Florin CIOFU, et al.
Published: (2022-05-01)

Corrosion-induced thickness diminution of an ageing bulk carrier
by: Nataša Kovač, et al.
Published: (2024-01-01)

Utilisation des résines échangeuses d’ions pour le nettoyage d’objets métalliques archéologiques ou historiques
by: Marietta Carlino, et al.
Published: (2021-05-01)

Corrosion mechanism of Al2O3–C stopper rod by calcium treated molten steel
by: Lidong Xing, et al.
Published: (2025-01-01)

An investigation on corrosion protection layers in pipelines transporting hydrocarbons
by: Giovanna Gabetta, et al.
Published: (2014-10-01)

Numerical investigation on stress corrosion cracking behavior of dissimilar weld joints in pressurized water reactor plants
by: Lingyan Zhao, et al.
Published: (2014-07-01)

Optimal Treatment Methods for Anti-Tartar Management in Circulating Water Systems
by: Mazouz Kherouf
Published: (2024-12-01)

Distribution of Corrosion Attack in Chloride Exposed Concrete – Summary of Field Observations
by: Baral Kedar, et al.
Published: (2024-12-01)

STUDY REGARDING THE INFLUENCE OF CORROSIVE AGENTS ON THE SURFACE OF METALLIC MATERIAL LIKE STEEL
by: OLGA POPA, et al.
Published: (2022-09-01)

In Situ Raman Spectroscopy for Early Corrosion Detection in Coated AA2024-T3
by: Adrienne K. Delluva, et al.
Published: (2024-12-01)

RESEARCH OF WITNESS SAMPLES OF SEAMLESS HOT-ROLLED PIPES AFTER TESTS IN WELLS OF OIL FIELDS OF RUP «ON «BELORUSNEFT» REGARDING THEIR CORROSION RESISTANCE
by: I. A. Kovaleva, et al.
Published: (2016-01-01)

The Effect of Steel Reinforcement Diameter on the Behavior of Concrete Beams with Corrosion
by: Joel Moreno-Herrera, et al.
Published: (2025-01-01)

Mechanical properties and corrosion behavior of circular oscillating laser direct energy deposited nickel-based superalloy after different heat-treatment processes
by: Yelin Xia, et al.
Published: (2025-01-01)

Prediction and evaluation of residual life of casing with corrosion defects
by: JIA Aoyin, et al.
Published: (2024-01-01)

Investigating the Formation of Trace Metal Contamination in Insulating Oil: From Electrical Erosion and Chemical Corrosion Perspectives
by: Feng Wang, et al.
Published: (2025-01-01)

Corrosion behavior of double-glow plasma copperizing coating on Q235 steel
by: Yang Z.-G., et al.
Published: (2020-01-01)

Study on Corrosion Characterization and Mechanism of the Monitoring Tubing under Air-Foam Flooding Injection Well
by: NING Chuang, ZHANG Liwei, TONG Zhangbing, JING Zhengzheng, YIN Zhifu
Published: (2024-12-01)

The analysis of bearing capacity of main pipeline in presence of corrosion defects
by: К. А. Vansovich, et al.
Published: (2019-06-01)

Macro- and micro-galvanic corrosion of friction stir welding 6061-T6 Al and C1100 Cu dissimilar joints
by: Yi-Ting Wu, et al.
Published: (2025-01-01)

Exploring corrosion protection of mild steel by ionic liquid functionalized graphene oxide: Gravimetric, electrochemical, and surface studies
by: M.Alharbi, et al.
Published: (2025-01-01)

Crack of a helicopter main rotor actuator attachment: failure analysis and lessons learned
by: L. Allegrucci, et al.
Published: (2013-09-01)

Identifying the Initial Corrosion Fatigue Failure Based on Dropping Electrochemical Potential
by: Anja Pfennig, et al.
Published: (2025-01-01)

Experimental investigation on effect of corrosion on curvature-ductility relationship of RCC member in flexure
by: P N Ojha, et al.
Published: (2022-05-01)

A comparison of high temperature corrosion behaviour between uncoated, Ni-Cr-Mo and Ni-Cr-Al-Y coated 316 stainless steel in ZnCl2-KCl environment
by: Pooja Mangaladevi, et al.
Published: (2025-03-01)

Electrochemical deposition of bimetallic sulfides on novel BDD electrode for bifunctional alkaline seawater electrolysis
by: Mingxu Li, et al.
Published: (2025-01-01)