High temperature initiation and propagation of cracks in 12%Cr-steel turbine disks
This work aims to study the crack propagation in 12%Cr steel for turbine disks. Creep Crack Growth (CCG) tests on CT specimens have been performed to define the proper fracture mechanics which describes the initiation of the crack propagation and the crack growth behaviour for the material at high t...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Gruppo Italiano Frattura
2013-09-01
|
| Series: | Fracture and Structural Integrity |
| Subjects: | |
| Online Access: | https://www.fracturae.com/index.php/fis/article/view/1176 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1841564279364386816 |
|---|---|
| author | S. Foletti A. Lo Conte S. Salgarollo F. Bassi A. Riva |
| author_facet | S. Foletti A. Lo Conte S. Salgarollo F. Bassi A. Riva |
| author_sort | S. Foletti |
| collection | DOAJ |
| description | This work aims to study the crack propagation in 12%Cr steel for turbine disks. Creep Crack
Growth (CCG) tests on CT specimens have been performed to define the proper fracture mechanics which
describes the initiation of the crack propagation and the crack growth behaviour for the material at high
temperature. Results have been used to study the occurrence of crack initiation on a turbine disk at the extreme
working temperature and stress level experienced during service, and validate the use of C* integral in
correlating creep growth rate on the disk component, in case C* is numerically calculated through FEM analysis
or calculated by the use of reference stress concept. |
| format | Article |
| id | doaj-art-e4d7d03f4a2f42c5aa3d37d148c451ac |
| institution | Kabale University |
| issn | 1971-8993 |
| language | English |
| publishDate | 2013-09-01 |
| publisher | Gruppo Italiano Frattura |
| record_format | Article |
| series | Fracture and Structural Integrity |
| spelling | doaj-art-e4d7d03f4a2f42c5aa3d37d148c451ac2025-01-02T23:01:04ZengGruppo Italiano FratturaFracture and Structural Integrity1971-89932013-09-01726High temperature initiation and propagation of cracks in 12%Cr-steel turbine disksS. FolettiA. Lo ConteS. SalgarolloF. BassiA. RivaThis work aims to study the crack propagation in 12%Cr steel for turbine disks. Creep Crack Growth (CCG) tests on CT specimens have been performed to define the proper fracture mechanics which describes the initiation of the crack propagation and the crack growth behaviour for the material at high temperature. Results have been used to study the occurrence of crack initiation on a turbine disk at the extreme working temperature and stress level experienced during service, and validate the use of C* integral in correlating creep growth rate on the disk component, in case C* is numerically calculated through FEM analysis or calculated by the use of reference stress concept.https://www.fracturae.com/index.php/fis/article/view/1176Creep Crack Growth |
| spellingShingle | S. Foletti A. Lo Conte S. Salgarollo F. Bassi A. Riva High temperature initiation and propagation of cracks in 12%Cr-steel turbine disks Fracture and Structural Integrity Creep Crack Growth |
| title | High temperature initiation and propagation of cracks in 12%Cr-steel turbine disks |
| title_full | High temperature initiation and propagation of cracks in 12%Cr-steel turbine disks |
| title_fullStr | High temperature initiation and propagation of cracks in 12%Cr-steel turbine disks |
| title_full_unstemmed | High temperature initiation and propagation of cracks in 12%Cr-steel turbine disks |
| title_short | High temperature initiation and propagation of cracks in 12%Cr-steel turbine disks |
| title_sort | high temperature initiation and propagation of cracks in 12 cr steel turbine disks |
| topic | Creep Crack Growth |
| url | https://www.fracturae.com/index.php/fis/article/view/1176 |
| work_keys_str_mv | AT sfoletti hightemperatureinitiationandpropagationofcracksin12crsteelturbinedisks AT aloconte hightemperatureinitiationandpropagationofcracksin12crsteelturbinedisks AT ssalgarollo hightemperatureinitiationandpropagationofcracksin12crsteelturbinedisks AT fbassi hightemperatureinitiationandpropagationofcracksin12crsteelturbinedisks AT ariva hightemperatureinitiationandpropagationofcracksin12crsteelturbinedisks |