Experimental investigation on fracture toughness of Al6061–graphite by using Circumferential Notched Tensile Specimens
This paper presents the experimental work carried out on the fracture behavior of aluminium 6061 (Al6061) and graphite particulate composites. The required specimens are prepared using stir casting method with graphite proportions ranging from 3 to 12 % by weight. The fracture behavior of Al6061-gra...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Gruppo Italiano Frattura
2017-01-01
|
| Series: | Fracture and Structural Integrity |
| Subjects: | |
| Online Access: | http://www.gruppofrattura.it/pdf/rivista/numero39/numero_39_art_25.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | This paper presents the experimental work carried out on the fracture behavior of aluminium 6061 (Al6061) and graphite particulate composites. The required specimens are prepared using stir casting method with graphite proportions ranging from 3 to 12 % by weight. The fracture behavior of Al6061-graphite particulate composites produced using stir casting method, was investigated by conducting experiments on Universal Testing Machine (UTM). Circumferential Notched Tensile (CNT) specimens were utilized to evaluate the fracture toughness of the composites. From the experiment the fracture toughness KIC= 15.85MPa m1/2 is obtained for Al6061-9% Graphite.
Further, the experimental results revealed that, except 12% graphite, the fracture toughness of Al6061-graphite was observed to increases with an increase in weight percentage of graphite. The experimental results reinforce that Al6061-graphite particulate MMCs are suitable for automotive and aerospace applications requiring high fracture toughness apart from good wear resistance. |
|---|---|