Baobab shell powder as a bio-filler in HDPE composites: mechanical, and physical properties
This study develops and characterizes high-density polyethylene (HDPE) composites reinforced with 0–20 wt% baobab shell powder (BSP) as a sustainable bio-filler. Composites were fabricated via compression molding and assessed for mechanical, physical, and chemical properties. XRF analysis revealed...
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
FLAYOO PUBLISHING HOUSE LIMITED
2025-08-01
|
| Series: | Recent Advances in Natural Sciences |
| Subjects: | |
| Online Access: | https://flayoophl.com/journals/index.php/rans/article/view/213 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | This study develops and characterizes high-density polyethylene (HDPE) composites reinforced with 0–20 wt% baobab shell powder (BSP) as a sustainable bio-filler. Composites were fabricated via compression molding and assessed for mechanical, physical, and chemical properties. XRF analysis revealed high metal oxide content in BSP—K2O (29.32%), MgO (16.27%), CaO (12.42%), Al2O3 (12.12%), and SiO2 (11.73%)—indicating multifunctional potential. FTIR confirmed lignocellulosic functional groups (O–H, C–H, C=O, C–O). Tensile strength peaked at 10.996 N/mm2 (20 wt%, +6.14% vs. neat HDPE); yield strength peaked at 26.35 N/mm2 (15 wt%), suggesting improved matrix interaction. Flexural strength dropped to 2.24 N/mm2 at 10 wt% but stabilized thereafter; elongation at break fell from 37.74% to 7.87%, indicating increased rigidity. Impact energy dropped from 4.0 J to 1.63 J, while hardness and density rose from 11.36 to 28.66 N/m2 and 0.87 to 0.93 g/cm3, respectively. Water absorption remained low until day 6, then rose sharply to ~20% (20 wt%) by day 8 due to interfacial degradation. Composites with ≤10 wt% BSP showed better moisture resistance. The results demonstrated that BSP enhances stiffness, hardness, and tensile strength but reduces ductility and impact resistance, making it suitable for non-structural applications in automotive, packaging, and sustainable construction.
|
|---|---|
| ISSN: | 1596-0544 1596-0757 |