Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels
The Space Shuttle wing-leading edge consists of panels that are made of reinforced carbon-carbon. Coating spallation was observed near the slip-side region of the panels that experience extreme heating. To understand this phenomenon, a root-cause investigation was conducted. As part of that inves...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Gruppo Italiano Frattura
2011-01-01
|
| Series: | Fracture and Structural Integrity |
| Subjects: | |
| Online Access: | http://www.gruppofrattura.it/pdf/rivista/numero15/numero_15_art_5.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1841564399231303680 |
|---|---|
| author | Kyongchan Song Dawn R. Phillips Norman F. Knight, Jr. Ivatury S. Raju |
| author_facet | Kyongchan Song Dawn R. Phillips Norman F. Knight, Jr. Ivatury S. Raju |
| author_sort | Kyongchan Song |
| collection | DOAJ |
| description | The Space Shuttle wing-leading edge consists of panels that are made of reinforced carbon-carbon. Coating spallation was observed near the slip-side region of the panels that experience extreme heating. To understand this phenomenon, a root-cause investigation was conducted. As part of that investigation, fracture mechanics analyses of the slip-side joggle regions of the hot panels were conducted. This paper presents an overview of the fracture mechanics analyses. |
| format | Article |
| id | doaj-art-794966f735cc46f0a5145d73a4c1a490 |
| institution | Kabale University |
| issn | 1971-8993 |
| language | English |
| publishDate | 2011-01-01 |
| publisher | Gruppo Italiano Frattura |
| record_format | Article |
| series | Fracture and Structural Integrity |
| spelling | doaj-art-794966f735cc46f0a5145d73a4c1a4902025-01-02T22:46:22ZengGruppo Italiano FratturaFracture and Structural Integrity1971-89932011-01-015153549Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panelsKyongchan SongDawn R. PhillipsNorman F. Knight, Jr.Ivatury S. RajuThe Space Shuttle wing-leading edge consists of panels that are made of reinforced carbon-carbon. Coating spallation was observed near the slip-side region of the panels that experience extreme heating. To understand this phenomenon, a root-cause investigation was conducted. As part of that investigation, fracture mechanics analyses of the slip-side joggle regions of the hot panels were conducted. This paper presents an overview of the fracture mechanics analyses.http://www.gruppofrattura.it/pdf/rivista/numero15/numero_15_art_5.pdfFracture mechanicsStrain energy release ratesRe-entry heatingOn orbit coldSpace ShuttleWing leading edge panels |
| spellingShingle | Kyongchan Song Dawn R. Phillips Norman F. Knight, Jr. Ivatury S. Raju Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels Fracture and Structural Integrity Fracture mechanics Strain energy release rates Re-entry heating On orbit cold Space Shuttle Wing leading edge panels |
| title | Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels |
| title_full | Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels |
| title_fullStr | Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels |
| title_full_unstemmed | Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels |
| title_short | Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels |
| title_sort | fracture mechanics analyses of the slip side joggle regions of wing leading edge panels |
| topic | Fracture mechanics Strain energy release rates Re-entry heating On orbit cold Space Shuttle Wing leading edge panels |
| url | http://www.gruppofrattura.it/pdf/rivista/numero15/numero_15_art_5.pdf |
| work_keys_str_mv | AT kyongchansong fracturemechanicsanalysesoftheslipsidejoggleregionsofwingleadingedgepanels AT dawnrphillips fracturemechanicsanalysesoftheslipsidejoggleregionsofwingleadingedgepanels AT normanfknightjr fracturemechanicsanalysesoftheslipsidejoggleregionsofwingleadingedgepanels AT ivaturysraju fracturemechanicsanalysesoftheslipsidejoggleregionsofwingleadingedgepanels |