FATIGUE BEHAVIOR OF WELDED STRUCTURES
Fatigue is a phenomenon consisting of the accumulation of stresses and deformations that cause cracking and sometimes dismantling or even destruction of structures as a consequence of applying variable loads over time as intensity and position ( load cycles). The applied loads have values below t...
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Academica Brancusi
2018-05-01
|
| Series: | Fiabilitate şi Durabilitate |
| Subjects: | |
| Online Access: | http://www.utgjiu.ro/rev_mec/mecanica/pdf/2018-01/07_Claudiu%20BABIS,%20%20Oana%20CHIVU,%20%20Andrei%20DIMITRESCU,%20Gabriel%20IACOBESCU,%20Anamaria%20FEIER,%20Augustin%20SEMENESCU%20-%20FATIGUE%20BEHAVIOR%20OF%20WELDED%20STRUCTURES.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Fatigue is a phenomenon consisting of the accumulation of stresses and deformations
that cause cracking and sometimes dismantling or even destruction of structures as a consequence
of applying variable loads over time as intensity and position ( load cycles). The applied loads
have values below the yield limit of the material from which the structure is made. These loads
having values below the yield limit, under static stresses, would not have the effect of causing the
fracture to fail. The paper aims is to present the basic mechanism of fatigue fracture by fatigue on
the one hand and on the other hand presents some experimental researches regarding the
evaluation of the quality of fillet welded joints of “GiurgeniVadulOii” bridge. |
|---|---|