Investigation of the microstructure, electrical and mechanical properties of Al-CNTs-B4C composite prepared by double-step stir casting for power transmission conductor
Monolithic aluminium alloy is a modern engineering material that is in high demand owing to its excellent performance and versatility. It has a high electrical conductivity, low density, high strength- to- weight ratio, and high resistance to corrosion. However, it lacks adequate resistance to creep...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
IOP Publishing
2024-01-01
|
| Series: | Materials Research Express |
| Subjects: | |
| Online Access: | https://doi.org/10.1088/2053-1591/ad8e30 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Monolithic aluminium alloy is a modern engineering material that is in high demand owing to its excellent performance and versatility. It has a high electrical conductivity, low density, high strength- to- weight ratio, and high resistance to corrosion. However, it lacks adequate resistance to creep, fatigue, stable microstructure, and strength at elevated temperatures. To overcome these deficiencies, aluminium matrix composites are developed. This work focuses on an experimental investigation of the microstructure, mechanical strength, and electrical conductivity of Al-CNTs-B _4 C composite consolidated by a double-step stir casting technique. An x-ray diffractometer, transmission electron microscopy, and a field-emission scanning electron microscope fitted with energy dispersive x-ray spectroscopy were used to characterize the start-up powders and the cast samples. A Brinell tester was used to measure the microhardness of the cast samples. A four-point probe meter was used to determine the electrical conductivity. The microstructural results revealed formation of Al _4 C _3 and Al _3 BC intermetallics, B _4 C phase and amorphous carbon precipitate. Marginally improved electrical conductivity of 33.33 × 10 ^7 S m ^−1 (65.1% IACS) was obtained with Al-5CNTs-15B _4 C, together with high microhardness of 725.72 MPa. The microhardness improved by 94.7% over monolithic pure Al. The double-step stir casting enhanced the homogenous dispersion of the reinforcements. The improvements in the mechanical properties and electrical conductivity were attributed to the synergy between B _4 C and CNTs which induced Orowan looping, load transfer effect, plastic deformation and dislocation pinning in the composite. It is recommended that this composite will perform creditably in power transmission. |
|---|---|
| ISSN: | 2053-1591 |