Analysis of corrosion damage in a boiler made of AISI 304L stainless steel
The corrosion damage near the welded joint in the boiler of AISI 304L stainless steel was analysed. During welding, heat tint was formed near the weld on the inner surface of the boiler, because shielded gas was not applied. Due to the presence of heat tint and crevice in the welded joint, pitting c...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Engineering Society for Corrosion, Belgrade, Serbia
2014-03-01
|
| Series: | Zaštita Materijala |
| Subjects: | |
| Online Access: | https://www.zastita-materijala.org/index.php/home/article/view/984 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1846130542059192320 |
|---|---|
| author | Biljana Bobić Bore Jegdić Bojan Gligorijević |
| author_facet | Biljana Bobić Bore Jegdić Bojan Gligorijević |
| author_sort | Biljana Bobić |
| collection | DOAJ |
| description | The corrosion damage near the welded joint in the boiler of AISI 304L stainless steel was analysed. During welding, heat tint was formed near the weld on the inner surface of the boiler, because shielded gas was not applied. Due to the presence of heat tint and crevice in the welded joint, pitting corrosion occurred which caused the perforation and leakage of the boiler. Several procedures are proposed to prevent localised forms of corrosion (pitting and crevice corrosion) near the welded joint of the boiler. |
| format | Article |
| id | doaj-art-2046b84a8a9b4b8d8ca019841114c5f9 |
| institution | Kabale University |
| issn | 0351-9465 2466-2585 |
| language | English |
| publishDate | 2014-03-01 |
| publisher | Engineering Society for Corrosion, Belgrade, Serbia |
| record_format | Article |
| series | Zaštita Materijala |
| spelling | doaj-art-2046b84a8a9b4b8d8ca019841114c5f92024-12-09T16:44:38ZengEngineering Society for Corrosion, Belgrade, SerbiaZaštita Materijala0351-94652466-25852014-03-01551333710.5937/ZasMat1401033B983Analysis of corrosion damage in a boiler made of AISI 304L stainless steelBiljana Bobić0Bore Jegdić1Bojan Gligorijević2Institute Goša, Belgrade, SerbiaInstitute Goša, Belgrade, SerbiaInstitute Goša, Belgrade, SerbiaThe corrosion damage near the welded joint in the boiler of AISI 304L stainless steel was analysed. During welding, heat tint was formed near the weld on the inner surface of the boiler, because shielded gas was not applied. Due to the presence of heat tint and crevice in the welded joint, pitting corrosion occurred which caused the perforation and leakage of the boiler. Several procedures are proposed to prevent localised forms of corrosion (pitting and crevice corrosion) near the welded joint of the boiler.https://www.zastita-materijala.org/index.php/home/article/view/984stainless steelsweldingheat tintcorrosion |
| spellingShingle | Biljana Bobić Bore Jegdić Bojan Gligorijević Analysis of corrosion damage in a boiler made of AISI 304L stainless steel Zaštita Materijala stainless steels welding heat tint corrosion |
| title | Analysis of corrosion damage in a boiler made of AISI 304L stainless steel |
| title_full | Analysis of corrosion damage in a boiler made of AISI 304L stainless steel |
| title_fullStr | Analysis of corrosion damage in a boiler made of AISI 304L stainless steel |
| title_full_unstemmed | Analysis of corrosion damage in a boiler made of AISI 304L stainless steel |
| title_short | Analysis of corrosion damage in a boiler made of AISI 304L stainless steel |
| title_sort | analysis of corrosion damage in a boiler made of aisi 304l stainless steel |
| topic | stainless steels welding heat tint corrosion |
| url | https://www.zastita-materijala.org/index.php/home/article/view/984 |
| work_keys_str_mv | AT biljanabobic analysisofcorrosiondamageinaboilermadeofaisi304lstainlesssteel AT borejegdic analysisofcorrosiondamageinaboilermadeofaisi304lstainlesssteel AT bojangligorijevic analysisofcorrosiondamageinaboilermadeofaisi304lstainlesssteel |