Effect of titanium and vanadium nano-carbide size on hydrogen embrittlement of ferritic steels
Abstract The effect of TiC and VC nano-precipitate size on the hydrogen embrittlement of ferritic steels was studied in this work. Steels containing two size distributions (10 nm or less and 10 - 100 nm) of TiC and VC carbides are subjected to tensile tests in-situ in an electrochemical hydrogen cha...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Nature Portfolio
2025-01-01
|
| Series: | npj Materials Degradation |
| Online Access: | https://doi.org/10.1038/s41529-024-00546-7 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Abstract The effect of TiC and VC nano-precipitate size on the hydrogen embrittlement of ferritic steels was studied in this work. Steels containing two size distributions (10 nm or less and 10 - 100 nm) of TiC and VC carbides are subjected to tensile tests in-situ in an electrochemical hydrogen charging environment. Hydrogen is found to be trapped in interstitial matrix sites on the precipitate/matrix interface with activation energies of 14 - 20 kJ/mol and inside misfit dislocation cores with energies of 27 - 37 kJ/mol. All steels are embrittled by 15 to 20%, except the TiC steel with semi-coherent carbides up to 100 nm, which is embrittled by 37%. This is caused by accelerated intergranular fracture as a result of hydrogen trapped in dislocation pile-ups around grain boundary precipitates. The steel with coherent VC nano-carbides retained the highest strength and ductility during in-situ testing. This is therefore the optimal carbide configuration for use in hydrogen environments. |
|---|---|
| ISSN: | 2397-2106 |