FAILURE ANALYSIS OF FRACTURE FOR CLUTCH SLEEVE PLATE
Sleeve plate of clutch disk is studied in this paper,according to the fracture problems of sleeve plate by carbonitriding and phosphating treatment,the fractured sleeve plate was analyzed by means of fracture macroscopic analysis,fracture microscopic analysis,metallographic analysis,hardness testing...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Editorial Office of Journal of Mechanical Strength
2018-01-01
|
| Series: | Jixie qiangdu |
| Subjects: | |
| Online Access: | http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2018.03.017 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1841535517556998144 |
|---|---|
| author | WANG XiaoLi MU Rui WANG CaiHong |
| author_facet | WANG XiaoLi MU Rui WANG CaiHong |
| author_sort | WANG XiaoLi |
| collection | DOAJ |
| description | Sleeve plate of clutch disk is studied in this paper,according to the fracture problems of sleeve plate by carbonitriding and phosphating treatment,the fractured sleeve plate was analyzed by means of fracture macroscopic analysis,fracture microscopic analysis,metallographic analysis,hardness testing and chemical composition analysis of material. The results show that the fracture of sleeve plate occurs before surface phosphating treatment,crack starts at left part of round window for sleeve plate,and it extends to run through the fracture in the process of production. In addition,due to cylindrical section is smaller and the surface area adopts hardening treatment,when the surface area is subjected to abnormal impact,it is very easy to cause the cracking of sleeve plate,especially the coarse structure leads to the increase of brittleness and it increases the probability of cracking of the parts. |
| format | Article |
| id | doaj-art-1ad2560c4d234ea996d0276744aa06ca |
| institution | Kabale University |
| issn | 1001-9669 |
| language | zho |
| publishDate | 2018-01-01 |
| publisher | Editorial Office of Journal of Mechanical Strength |
| record_format | Article |
| series | Jixie qiangdu |
| spelling | doaj-art-1ad2560c4d234ea996d0276744aa06ca2025-01-15T02:32:00ZzhoEditorial Office of Journal of Mechanical StrengthJixie qiangdu1001-96692018-01-014060761230601708FAILURE ANALYSIS OF FRACTURE FOR CLUTCH SLEEVE PLATEWANG XiaoLiMU RuiWANG CaiHongSleeve plate of clutch disk is studied in this paper,according to the fracture problems of sleeve plate by carbonitriding and phosphating treatment,the fractured sleeve plate was analyzed by means of fracture macroscopic analysis,fracture microscopic analysis,metallographic analysis,hardness testing and chemical composition analysis of material. The results show that the fracture of sleeve plate occurs before surface phosphating treatment,crack starts at left part of round window for sleeve plate,and it extends to run through the fracture in the process of production. In addition,due to cylindrical section is smaller and the surface area adopts hardening treatment,when the surface area is subjected to abnormal impact,it is very easy to cause the cracking of sleeve plate,especially the coarse structure leads to the increase of brittleness and it increases the probability of cracking of the parts.http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2018.03.017Sleeve plateFracture failureMacroscopic analysisMicroscopic analysis |
| spellingShingle | WANG XiaoLi MU Rui WANG CaiHong FAILURE ANALYSIS OF FRACTURE FOR CLUTCH SLEEVE PLATE Jixie qiangdu Sleeve plate Fracture failure Macroscopic analysis Microscopic analysis |
| title | FAILURE ANALYSIS OF FRACTURE FOR CLUTCH SLEEVE PLATE |
| title_full | FAILURE ANALYSIS OF FRACTURE FOR CLUTCH SLEEVE PLATE |
| title_fullStr | FAILURE ANALYSIS OF FRACTURE FOR CLUTCH SLEEVE PLATE |
| title_full_unstemmed | FAILURE ANALYSIS OF FRACTURE FOR CLUTCH SLEEVE PLATE |
| title_short | FAILURE ANALYSIS OF FRACTURE FOR CLUTCH SLEEVE PLATE |
| title_sort | failure analysis of fracture for clutch sleeve plate |
| topic | Sleeve plate Fracture failure Macroscopic analysis Microscopic analysis |
| url | http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2018.03.017 |
| work_keys_str_mv | AT wangxiaoli failureanalysisoffractureforclutchsleeveplate AT murui failureanalysisoffractureforclutchsleeveplate AT wangcaihong failureanalysisoffractureforclutchsleeveplate |